World of Steel - Stainless Steel Composition
17-4PH 0.025 0.6 0.3 0 0.01 4.2 15.1 3.1 0 200   Nb+Ta=
0.045 0.8 0.4 0.04 0.02 4.4 15.5 3.3 0.2 350   0.25/0.30
201E 0.08 7.5 0.4 0 0 3.3 15.6 0 0 1700    
201M 0.08 7.5 0.5 0 0 3.1 16.1 0.3 0 1700    
  0.1 8 0.7 0.06 0.01 3.4 16.4 0.5 0.3 1900    
201S 0.08 8.2 0.4 0 0 0.3 14 1.7 0 1500   Aim Ni eqv >12
  0.1 8.5 0.6 0.08 0.015 0.5 14.5 1.9 0.3 1700    
201WR06 0.08 8.1 0.4 0 0 0.6 14 1.7 0 1500   Aim Ni eqv >12
  0.1 8.3 0.6 0.08 0.015 0.8 14.5 1.9 0.3 1700    
201WR09 0.08 8.1 0.4 0 0 0.9 14 1.7 0 1400   Aim Ni eqv >12
  0.1 8.3 0.6 0.08 0.015 1.1 14.5 1.9 0.3 1600    
201WR2 0.06 8.1 0.4 0 0 2 14.5 1.6 0 1300    
  0.08 8.3 0.6 0.07 0.015 2.2 14.8 1.8 0.3 1500    
 
201WR3 0.04 8.3 0.4 0 0 3.05 14.5 1.7 0 1300    
  0.06 8.6 0.6 0.07 0.01 3.3 15 1.9 0.3 1500    
201WR3HS 0.04 8.3 0.4 0 0.015 3.05 14.5 1.7 0 1300    
  0.06 8.6 0.6 0.07 0.03 3.3 15 1.9 0.3 1500    
201WR 0.08 8.2 0.4 0 0 0.3 14 1.7 0 1500   Aim Ni eqv >12
  0.1 8.5 0.6 0.08 0.015 0.5 14.5 1.9 0.3 1700    
302 0.08 1.1 0.25 0 0 8.1 18 0 0 500    
  0.1 1.3 0.45 0.04 0.01 8.2 18.3 0.3 0.3 700    
302BR 0.09 0.3 0.3 0 0 8.1 18 0.15 0 700    
  0.11 0.5 0.5 0.04 0.01 8.2 18.3 0.3 0.3 900    
302HQ 0.015 0.6 0.25 0 0 9.5 17.3 3.25 0 0    
  0.025 0.8 0.45 0.04 0.01 9.7 17.6 3.5 0.3 250    
302HQCr18 0.015 0.6 0.25 0 0 9.5 18.1 3.25 0 0    
  0.025 0.8 0.45 0.04 0.01 9.7 18.3 3.5 0.3 250    
302K 0.09 1.5 0.25 0 0 8.1 17.1 0 0 500    
  0.11 1.7 0.45 0.04 0.01 8.2 17.4 0.3 0.3 700    
302RR 0.07 0.5 0.3 0 0 8.2 18.1 0 0 600    
  0.09 0.75 0.5 0.04 0.01 8.4 18.5 0.3 0.3 800    
302V 0.06 0.3 0.3 0 0 8.1 18.1 0 0 600    
  0.08 0.5 0.45 0.04 0.01 8.2 18.3 0.3 0.3 800    
303Cu 0.035 1.9 0.25 0 0.28 8.5 17.2 2 0 400   CaSi inj must
  0.055 2 0.45 0.04 0.3 8.8 17.6 2.4 0.3 600    
303EHS 0.035 1.9 0.25 0 0.3 8.3 17.2 0 0 300   CaSi inj must
  0.055 2 0.45 0.04 0.33 8.6 17.6 0.3 0.3 500    
303NMHS 0.03 1.9 0.15 0 0.31 8.2 17.5 0 0 600   CaSi inj must
  0.05 2 0.3 0.04 0.34 8.4 17.9 0.3 0.3 800    
303NMHSCu 0.03 1.9 0.15 0 0.31 8.5 17.3 0.4 0 350   CaSi inj must
  0.05 2 0.3 0.04 0.34 8.7 17.7 0.6 0.3 550    
303PMS 0.05 1.9 0.25 0 0.28 8.6 17.2 0.3 0 0   CaSi inj must
  0.07 2 0.45 0.04 0.32 8.9 17.6 0.5 0.3 250    
303USA 0.02 1.9 0.3 0 0.24 8.9 17.2 0 0 0   CaSi inj must
  0.035 2 0.5 0.04 0.27 9.2 17.6 0.3 0.3 300   AIM S = 0.25 MAX
303V 0.03 1.9 0.25 0 0.31 8.1 17.1 0 0 300   CaSi inj must
  0.05 2 0.45 0.04 0.34 8.3 17.4 0.3 0.3 500    
303XM 0.035 1.9 0.25 0 0.31 8.9 17.2 0.4 0 0   CaSi inj must
  0.055 2 0.45 0.04 0.34 9.1 17.6 0.6 0.3 300    
304 0.05 1.3 0.25 0 0 8 18.1 0 0 400    
  0.07 1.5 0.45 0.04 0.015 8.1 18.4 0.3 0.3 600    
304Cu 0.05 1.3 0.3 0 0 8 18.1 0.4 0 400    
  0.07 1.5 0.5 0.04 0.015 8.2 18.4 0.6 0.3 600    
304E 0.04 1.4 0.25 0 0 8.6 18.1 0 0 400    
  0.06 1.6 0.45 0.04 0.02 8.8 18.3 0.3 0.3 600    
304ECu 0.02 1.6 0.25 0 0 8.7 18.4 0.9 0 0   CWH factor=
  0.028 1.8 0.45 0.04 0.01 9 18.8 1.1 0.3 250   94 -107
304ED 0.03 1.2 0.25 0 0 8.5 18.1 0 0 400    
  0.05 1.4 0.45 0.4 0.015 8.8 18.4 0.3 0.3 600    
304EHS 0.03 1.5 0.25 0 0.02 8.6 18.1 0 0 400   CaSi inj must
  0.05 1.7 0.45 0.04 0.03 8.8 18.3 0.3 0.3 600    
304EN 0.03 1.1 0.25 0 0 9.1 18.1 0 0 300    
  0.05 1.3 0.45 0.04 0.01 9.4 18.4 0.25 0.2 500    
304ENM 0.05 1.6 0.4 0 0 8.8 18.1 0 0 700    
  0.07 1.8 0.6 0.04 0.01 9 18.4 0.3 0.3 900    
304H 0.06 1 0.3 0 0 8.1 18.1 0 0 400    
  0.08 1.2 0.5 0.035 0.01 8.2 18.4 0.25 0.2 600    
304HC 0.025 1.4 0.25 0 0 8.2 18.1 2.2 0 300    
  0.045 1.6 0.45 0.04 0.02 8.4 18.4 2.4 0.3 500    
304HS 0.04 1.3 0.25 0 0.02 8 18.1 0 0 400   CaSi inj must
  0.06 1.5 0.45 0.04 0.03 8.1 18.4 0.3 0.3 600    
304HSP 0.045 1 0.3 0 0 9.6 18.1 0 0 0    
  0.065 1.2 0.5 0.04 0.01 9.9 18.4 0.25 0.2 200    
304HU 0.06 0.7 0.2 0 0 8.3 18.1 0 0 400    
  0.08 0.8 0.3 0.04 0.01 8.5 18.4 0.3 0.3 600    
304L 0 1.5 0.25 0 0 8.5 18.1 0 0 400    
  0.028 1.7 0.45 0.04 0.01 8.7 18.4 0.3 0.3 550    
304LAHS 0 1.6 0.25 0 0.015 8.1 18.1 0 0 600   CaSi inj must
  0.028 1.8 0.45 0.04 0.03 8.3 18.3 0.3 0.3 800    
304LC 0 1.6 0.3 0 0.01 8.9 18.5 0 0 600    
  0.028 1.8 0.5 0.04 0.02 9.2 18.9 0.3 0.3 800    
304LE 0 1.6 0.25 0 0 9.1 18.2 0 0 0   CaSi inj must
  0.028 1.8 0.45 0.04 0.01 9.4 18.4 0.3 0.3 250    
304LEHS 0 1.6 0.25 0 0.02 9.1 18.1 0 0 0   CaSi inj must
  0.028 1.8 0.45 0.04 0.03 9.4 18.4 0.3 0.3 250    
304LER 0 1.5 0.25 0 0 9.3 18.6 0 0 0   P+S= 0.03 max
  0.025 1.7 0.45 0.025 0.01 9.6 18.9 0.25 0.25 300    
304LHS 0 1.5 0.25 0 0.02 8.5 18.1 0 0 400   CaSi inj must
  0.028 1.7 0.45 0.04 0.03 8.7 18.4 0.3 0.3 600    
304LHSCu 0 1.5 0.25 0 0.02 8.5 18.1 0.4 0 400   CaSi inj must
  0.028 1.7 0.45 0.04 0.03 8.7 18.4 0.6 0.3 600    
304LMS 0 1.5 0.25 0 0.01 8.5 18.1 0 0 400   CaSi inj must
  0.028 1.7 0.45 0.04 0.02 8.7 18.3 0.3 0.3 600    
304LN 0 1.4 0.25 0 0 10.2 18.3 0 0 0    
  0.028 1.6 0.45 0.04 0.01 10.4 18.5 0.3 0.3 250    
304LNHS 0 0.7 0.25 0 0.02 10.2 18.3 0 0 0   CaSi inj must
  0.028 0.9 0.45 0.04 0.03 10.4 18.5 0.3 0.3 250    
304LNSP 0.02 1 0.3 0 0 10.1 18.3 0 0 0    
  0.028 1.2 0.45 0.028 0.01 10.4 18.7 0.3 0.15 250    
304LR 0 1.5 0.25 0 0 8.8 18.1 0 0 300    
  0.028 1.7 0.45 0.04 0.01 9 18.3 0.3 0.3 500    
304LRHS 0 1.3 0.3 0 0.02 9.1 18.1 0 0 400   CaSi inj must
  0.028 1.6 0.5 0.04 0.03 9.4 18.4 0.3 0.3 600    
304LU 0 1.2 0.3 0 0 9.5 18.1 0.4 0.3 0    
  0.028 1.4 0.5 0.04 0.01 9.7 18.4 0.6 0.5 300    
304M 0.04 0.8 0.25 0 0 9.1 18.1 0 0 300    
  0.06 1 0.45 0.04 0.01 9.3 18.4 0.3 0.3 500    
304ME 0.025 1.1 0.25 0 0 9.1 18.1 0 0 300   CaSi inj must
  0.045 1.3 0.45 0.035 0.01 9.4 18.4 0.3 0.3 500    
304MK 0.03 1.2 0.25 0 0 9.1 18.1 0 0 300    
  0.05 1.4 0.45 0.04 0.01 9.3 18.4 0.3 0.3 500    
304MU 0.04 1.6 0.2 0 0 8.1 18.1 0 0 400    
  0.06 1.8 0.3 0.04 0.01 8.4 18.4 0.3 0.3 600    
304NM 0.05 1.6 0.4 0 0 8 18.1 0 0 700    
  0.07 1.8 0.6 0.04 0.02 8.1 18.4 0.3 0.3 900    
304NMCU 0.05 1.6 0.4 0 0 8 18.1 0.7 0 600    
  0.07 1.8 0.6 0.04 0.01 8.1 18.4 0.9 0.3 800    
304NMHS 0.05 1.6 0.4 0 0.02 8 18.1 0 0 700   CaSi inj must
  0.07 1.8 0.6 0.04 0.03 8.2 18.4 0.3 0.3 900    
304NMHSCu 0.05 1.6 0.4 0 0.02 8 18.1 0.4 0 700   CaSi inj must
  0.07 1.8 0.6 0.04 0.03 8.1 18.4 0.6 0.3 900    
304S LP 0.04 1.4 0.25 0 0 8.1 18.1 0 0 400   Low Phosphorous
  0.06 1.6 0.45 0.025 0.015 8.2 18.4 0.3 0.3 600   Aim N2 =500 ppm
304S 0.04 1.4 0.25 0 0 8.1 18.1 0 0 400    
  0.06 1.6 0.45 0.04 0.015 8.2 18.4 0.3 0.3 600    
304SCu 0.05 1.4 0.25 0 0 8 18.1 0.4 0 600    
  0.07 1.6 0.45 0.04 0.01 8.2 18.4 0.6 0.3 800    
304SD 0.05 1 0.25 0 0 8.3 18.1 0 0 400    
  0.07 1.2 0.45 0.04 0.01 8.5 18.4 0.3 0.3 600    
304SDCu 0.05 1 0.25 0 0 8.2 18 0.6 0 300    
  0.07 1.2 0.45 0.04 0.01 8.4 18.4 0.9 0.3 500    
304SM 0.06 1.2 0.3 0 0 8.4 18.1 0 0 300    
  0.08 1.4 0.5 0.03 0.02 8.6 18.4 0.3 0.3 500    
304SR 0.04 1.4 0.25 0 0 8.1 18.1 0 0 400    
  0.06 1.6 0.45 0.04 0.015 8.2 18.4 0.3 0.3 600    
304V 0.03 1.5 0.2 0 0 8 18.1 0 0 400    
  0.05 1.7 0.3 0.04 0.015 8.1 18.4 0.3 0.3 600    
305 0 1.7 0.3 0 0.015 10.7 18.3 0 0 0   CaSi inj must
  0.025 1.9 0.5 0.04 0.025 10.9 18.6 0.3 0.3 250    
308LER Lsi-RR 0 1.6 0.1 0 0 9.8 19.6 0 0 500   P+S=0.03 max
  0.018 1.9 0.2 0.02 0.01 10.2 19.9 0.25 0.2 700    
308LER Lsi-VW 0 1.6 0 0 0 9.8 19.6 0 0 500   P+S= 0.03 max
  0.018 1.9 0.1 0.02 0.01 10.2 19.9 0.2 0.25 700   Co = 0.15 max
308LER Msi 0 1.6 0.35 0 0 10.1 19.6 0 0 400   P+S= 0.03 max
  0.018 1.9 0.45 0.02 0.01 10.3 19.8 0.15 0.2 600   Co = 0.15 max
309LER 0 1.7 0.3 0 0 13.7 23.1 0 0 500   P+S= 0.03 max
  0.018 1.9 0.45 0.02 0.01 13.9 23.4 0.25 0.2 700    
309S 0.015 1.6 0.25 0 0 13.6 22.1 0.35 0 350   CaSi inj must
  0.025 1.8 0.35 0.025 0.005 13.9 22.4 0.5 0.3 550    
310S 0.035 1.2 0.6 0 0 19.2 25.4 0 0 0    
  0.055 1.4 0.75 0.04 0.005 19.5 25.9 0.3 0.3 200    
314 0.015 1.45 2.3 0 0 19.9 23 0 0 0    
  0.035 1.65 2.5 0.03 0.01 20.3 23.6 0.3 0.1 300    
316(LowP) 0.04 1.3 0.3 0 0 10.1 16.5 0 2.02 400    
  0.06 1.5 0.45 0.025 0.01 10.3 16.7 0.3 2.2 600    
316 0.04 1.3 0.3 0 0 10.1 16.5 0 2.02 400    
  0.06 1.5 0.5 0.04 0.01 10.3 16.7 0.3 2.2 600    
316E 0.04 1.2 0.25 0 0 10.6 16.6 0 2.02 300    
  0.06 1.4 0.45 0.04 0.01 10.9 17 0.3 2 500    
316EHS 0.04 1.2 0.3 0 0.02 10.6 16.6 0 2.02 300   CaSi inj must
  0.06 1.4 0.5 0.04 0.03 10.9 17 0.3 2 500    
316EN 0.025 1.2 0.25 0 0 11.1 16.8 0 2.02 250    
  0.045 1.4 0.45 0.04 0.01 11.3 17.2 0.3 2.2 450    
316EP 0.04 1.2 0.25 0 0 10.6 16.8 0 2.02 300    
  0.06 1.4 0.45 0.04 0.015 10.9 17.2 0.3 2.2 500    
316ESPL 0.045 1 0.25 0 0 12.4 17.6 0 2.5 0    
  0.065 1.2 0.45 0.04 0.01 12.6 18 0.3 2.7 250    
316G 0.04 1.7 0.25 0 0 10.1 16.5 0 2.02 700    
  0.06 1.9 0.45 0.04 0.01 10.3 16.9 0.3 2.2 900    
316HS 0.04 1.3 0.3 0 0.02 10.1 16.5 0 2.02 400   CaSi inj must
  0.06 1.5 0.5 0.04 0.03 10.3 16.7 0.3 2.2 600    
316L 0 1.2 0.3 0 0 10.1 16.5 0 2.02 550   CaSi inj must
  0.028 1.4 0.5 0.04 0.01 10.4 16.7 0.3 2.2 750    
316LBB 0 1.2 0.3 0 0.005 10.1 16.1 0 2.02 550   CaSi inj must
  0.028 1.4 0.5 0.04 0.015 10.4 16.5 0.3 2.2 750    
316LC 0 1.5 0.3 0 0.01 10.6 16.5 0 2.02 400    
  0.028 1.7 0.5 0.04 0.02 10.9 16.9 0.2 2.2 600    
316LE 0 1.2 0.25 0 0 11.1 16.8 0 2.02 200    
  0.028 1.4 0.45 0.04 0.01 11.4 17.2 0.3 2.2 350    
316LEHS 0 1.2 0.25 0 0.02 11.1 16.8 0 2.02 200   CaSi inj must
  0.028 1.4 0.45 0.04 0.03 11.4 17.2 0.3 2.2 350    
316LER Msi-RR 0 1.7 0.35 0 0 12.6 18.6 0 2.22 400   P+S = 0.03 max.
  0.018 1.9 0.5 0.02 0.01 12.8 18.9 0.15 2.4 600   Co = 0.15 max
316LER Msi-VW 0 1.7 0.35 0 0 13.1 19.1 0 2.52 600   P+S= 0.03 max
  0.018 1.9 0.5 0.02 0.01 13.4 19.4 0.15 2.7 800   Co = 0.15 max
316LG 0 1.4 0.3 0 0.01 10.2 16.5 0 2.02 600   CaSi inj must
  0.028 1.6 0.5 0.04 0.02 10.4 16.7 0.3 2.2 800    
316LGHS 0 1.4 0.3 0 0.02 10.2 16.5 0 2.02 600   CaSi inj must
  0.028 1.6 0.5 0.04 0.03 10.4 16.7 0.3 2.2 800    
316LHS 0 1.2 0.3 0 0.02 10.1 16.5 0 2.02 550    
  0.028 1.4 0.5 0.04 0.03 10.4 16.7 0.3 2.2 750    
316LHSCu 0 1.2 0.3 0 0.02 10.1 16.5 0.4 2.02 550   CaSi inj must
  0.028 1.4 0.5 0.04 0.03 10.4 16.7 0.6 2.2 750    
316LK 0.015 1.3 0.25 0 0.01 11.1 17 0 2.1 600   CaSi inj must
  0.03 1.5 0.4 0.04 0.02 11.3 17.3 0.3 2.2 800    
316LMER 0 1.5 0.3 0 0 10.5 16.5 0 2.02 550   Co  0 .05 max
  0.018 1.7 0.5 0.04 0.01 10.7 16.7 0.3 2.2 750    
316LMS 0 1.2 0.3 0 0.007 10.1 16.5 0 2.02 550   CaSi inj must
  0.028 1.4 0.5 0.04 0.017 10.4 16.7 0.3 2.2 750    
316LRHS 0 1.2 0.3 0 0.02 11.1 16.8 0 2.02 250   CaSi inj must
  0.028 1.4 0.5 0.04 0.03 11.4 17.2 0.3 2.2 350    
316LSP 0.02 1.3 0.3 0 0 10.1 16.5 0 2.02 400    
  0.028 1.5 0.45 0.04 0.01 10.4 16.7 0.3 2.2 600    
316LU 0 1.2 0.3 0 0 11.1 16.5 0 2.02 0    
  0.028 1.4 0.5 0.03 0.01 11.4 16.7 0.3 2.2 350    
316NG 0.03 1.3 0.25 0 0 10.3 16.6 0 2.02 500    
  0.05 1.5 0.45 0.04 0.02 10.5 16.9 0.3 2.2 700    
316NMHSCu 0.04 1.7 0.25 0 0.02 10.1 16.5 0.4 2.02 700   CaSi inj must
  0.06 1.9 0.45 0.04 0.03 10.3 16.8 0.6 2.2 900    
316RU 0.05 1.2 0.25 0 0 10.6 16.6 0 2.02 250    
  0.07 1.4 0.45 0.03 0.01 10.9 17 0.3 2.2 450    
316Ti 0.02 1.5 0.3 0 0 11 16.6 0 2.02 0 Ti Al = .03/.05
  0.04 1.7 0.5 0.04 0.01 11.4 17 0.3 2.2 200 0.15/.25 Ti = 5x %C min
317LN 0.02 1 0.45 0 0 13.8 18 0 4.1 1100   CaSi inj must
  0.03 1.3 0.6 0.04 0.01 14 18.3 0.25 4.3 1300    
321 0 1.6 0.3 0 0.01 9.3 17.1 0 0 0 Ti Al = .03/.05
  0.03 1.8 0.45 0.04 0.02 9.5 17.4 0.3 0.3 200 .30/.40 Ti = 5x%(C+N) min
321SP 0.02 1 0.3 0 0 10.5 18.1 0 0 0 Ti Al = .03/.05
  0.04 1.2 0.5 0.04 0.01 10.8 18.4 0.3 0.15 200 .10/.18 Ti = 5x %C min
321SPL 0.03 1.6 0.3 0 0 9.4 17.1 0 0 0 Ti Al = .03/.05
  0.05 1.8 0.45 0.025 0.01 9.6 17.4 0.3 0.3 200 .50/.60 Ti = 0.50 min
405 0.04 0.75 0.4 0 0 0 11.6 0 0 0 Al  
  0.06 0.9 0.6 0.04 0.01 0.25 12 0.25 0.15 200 .12/.18  
409Ti 0 0.4 0.3 0 0 0.75 11 0 0 0   Ti = 16 X %C min
  0.025 0.6 0.5 0.04 0.03 1 11.4 0.2 0.2 200    
410 0.1 0.6 0.3 0 0.01 0 12.5 0 0 0   CaSi inj must
  0.12 0.85 0.5 0.04 0.02 0.25 13 0.3 0.3 200    
410B/403 0.1 0.6 0.3 0 0.01 0 12.5 0 0 0   CaSi inj must
  0.12 0.85 0.5 0.04 0.02 0.25 13 0.3 0.3 200    
410G 0.08 0.6 0.4 0 0 0 13.1 0 0 0   CaSi inj must
  0.1 0.85 0.6 0.04 0.015 0.25 13.4 0.3 0.3 200    
410HS 0.1 0.6 0.4 0 0.02 0 12.5 0 0 0   CaSi inj must
  0.12 0.85 0.6 0.04 0.03 0.25 13 0.3 0.3 200    
410SP 0.04 0.75 0.4 0 0 0 12 0 0 0   CaSi inj must
  0.06 0.9 0.6 0.03 0.01 0.25 12.5 0.25 0.15 200    
410VS 0.13 0.6 0.4 0 0.02 0 12.5 0 0 0   CaSi inj must
  0.15 0.85 0.6 0.04 0.03 0.25 13 0.3 0.3 200    
410W 0.08 0.6 0.4 0 0 0 12.5 0 0 0   CaSi inj must
  0.1 0.85 0.6 0.04 0.02 0.25 13 0.3 0.3 200    
416 0.12 1.1 0.4 0 0.29 0 12.2 0 0 0    
  0.14 1.2 0.6 0.04 0.33 0.25 12.6 0.3 0.3 200    
416V 0.12 1.1 0.2 0 0.15 0 12.2 0 0 0    
  0.15 1.2 0.4 0.04 0.2 0.25 12.6 0.3 0.3 200    
416XM 0.1 1.1 0.4 0 0.31 0 12.2 0 0 0   CaSi inj must
  0.12 1.2 0.6 0.04 0.34 0.25 12.6 0.25 0.25 200    
420 0.15 0.6 0.4 0 0 0 12.2 0 0 0    
  0.18 0.85 0.6 0.04 0.02 0.25 12.6 0.3 0.3 200    
420G 0.2 0.6 0.4 0 0.02 0.5 13 0 0 0    
  0.22 0.85 0.6 0.04 0.03 0.7 13.5 0.3 0.3 200    
420VS 0.2 0.6 0.4 0 0.02 0 12.7 0 0 0   CaSi inj must 
  0.22 0.85 0.6 0.04 0.03 0.25 12.9 0.3 0.3 200    
430F 0.05 1.1 0.4 0 0.25 0 16.1 0 0 0    
  0.07 1.25 0.6 0.04 0.29 0.25 16.4 0.3 0.3 200    
430FDIN 0.12 1.3 0.4 0 0.25 0 15.6 0 0.22 0   CaSi inj must
  0.15 1.5 0.6 0.04 0.29 0.25 16.1 0.3 0.3 200    
430K 0.03 0.35 0.3 0 0 0 16.2 0 0 0    
  0.05 0.5 0.5 0.04 0.03 0.25 16.6 0.3 0.3 250    
430KS 0.03 0.35 0.3 0 0 0 16.6 0 0 0    
  0.05 0.5 0.5 0.04 0.01 0.5 16.9 0.3 0.3 250    
430L 0 0.35 0.3 0 0 0 16.6 0 0 150    
  0.025 0.5 0.5 0.035 0.01 0.25 16.9 0.3 0.3 300    
430USA 0 0.35 0.3 0 0 0 16.5 0 0 0    
  0.03 0.5 0.5 0.035 0.01 0.05 16.9 0.3 0.3 200    
431HS 0.13 0.6 0.3 0 0.02 1.35 15.5 0 0 0   CaSi inj must
  0.16 0.8 0.5 0.04 0.03 1.5 16 0.3 0.3 200    
431VHS 0.13 0.6 0.3 0 0.02 2 15.7 0 0 0    
  0.15 0.8 0.5 0.04 0.03 2.2 16.2 0.3 0.3 200    
434 0.03 0.4 0.4 0 0.02 0 16.4 0 0.9 0   CaSi inj must
  0 0.3 0.3 0 0 0 16.3 0.85 0 0    
434A 0.03 0.5 0.5 0.035 0.01 0.25 16.5 1 0.3 250    
  0.05 0.6 0.6 0.04 0.03 0.3 16.8 0.3 1.1 200    
AISI201 0.08 7.1 0.4 0 0 3.6 16.1 0.3 0 1400    
  0.1 7.4 0.6 0.06 0.01 3.8 16.4 0.5 0.3 1600    
AISI202 0.08 7.5 0.5 0 0 4.1 17.1 0 0 1400    
  0.1 8 0.7 0.06 0.015 4.6 17.5 0.3 0.3 1600    
SI3DM 0.06 9 0.4 0 0 1.8 15 1.7 0 1400   Aim Ni eqv >12
  0.08 9.4 0.6 0.07 0.015 2 15.4 1.9 0.3 1600    
TP 316Ti 0.015 1.6 0.3 0 0 11.8 16.6 0 2.02 0 Ti Al = .025/.045
  0.03 1.8 0.5 0.04 0.01 12 16.8 0.5 2.2 200 0.20/.30 Ti= 5x%(C+N2)min
TP304H 0.04 1.7 0.25 0 0 8.5 18.3 0 0 700    
  0.06 1.9 0.45 0.04 0.01 8.7 18.6 0.3 0.3 900    
TP304L 0 1.2 0.3 0 0 10.2 18.3 0 0 600    
  0.02 1.4 0.45 0.035 0.01 10.4 18.6 0.3 0.3 800    
TP316H 0.04 1.3 0.25 0 0 11.1 16.5 0 2.02 400    
  0.06 1.5 0.4 0.04 0.01 11.4 16.8 0.5 2.2 600    
TP316L 0 1.2 0.25 0 0 11.4 16.8 0 2.02 250    
  0.028 1.4 0.45 0.04 0.01 11.8 17.2 0.3 2.2 350    
TP410S 0.04 0.55 0.35 0 0 0 12.1 0 0 0    
  0.06 0.7 0.5 0.035 0.01 0.25 12.5 0.2 0.2 200    
XX 0 0 0 0 0 0 0 0 0 0 0 0
  0 0 0 0 0 0 0 0 0 0 0 0
 





     Home  |  About  |  Contact  |  Terms of Use  |  Privacy Policy
World of Steel® is a Registered Trademark in USA, China, India and EU